Wyświetlenia: 0 Autor: Edytor witryny Czas publikacji: 22.10.2025 Pochodzenie: Strona
| Model lasera | RFL-3000(34u) | Współczynnik optyczny głowicy tnącej | 150Kolimacja 100 / Ogniskowa 150 | |||||
| Tworzywo | Grubość [mm] | Prędkość [m/min] | Moc [W] | Gaz | Ciśnienie powietrza [bar] | Dysza [mm] | Pozycja ogniskowa [mm] | Wysokość cięcia [mm] |
| Stal węglowa | 1 | 40-50 | 6600 | N₂/powietrze | 12 | 1,5 S | 0 | 1 |
| 2 | 25-30 | 12 | 2,0 S | -1 | 0.5 | |||
| 3 | 18-24 | 14 | 2,0 S | -1.5 | 0.5 | |||
| 4 | 12-16 | 14 | 2,0 S | -2 | 0.5 | |||
| 5 | 8-10 | 16 | 3,0 S | -2.5 | 0.5 | |||
| 6 | 7-8 | 16 | 3,5 S | -3 | 0.5 | |||
| Stal węglowa | 3 | 3.6-4.2 | 2400 | O₂ | 0.6 | 1.2E | +3 | 0.8 |
| 4 | 3,3-3,8 | 2400 | 0.6 | 1.2E | +3 | 0.8 | ||
| 5 | 3-3.6 | 3500 | 0.6 | 1.2E | +3 | 0.8 | ||
| 6 | 2.7-3.2 | 3300 | 0.6 | 1.2E | +3 | 0.8 | ||
| 8 | 2,2-2,5 | 4200 | 0.6 | 1.2E | +3 | 0.8 | ||
| 10 | 2,0-2,3 | 6600 | 0.6 | 1.2E | +4 | 0.8 | ||
| 12 | 0,9-1 | 2400 | 0.6 | 3.0D | +2,5 | 0.8 | ||
| 12 | 1,9-2,1 | 6600 | 0.6 | 1.2E | +5 | 0.8 | ||
| 14 | 0,8-0,9 | 2400 | 0.6 | 3.5D | +2,5 | 0.8 | ||
| 14 | 1,4-1,7 | 6600 | 0.6 | 1,4E | +5 | 1 | ||
| 16 | 0,8-0,9 | 2400 | 0.6 | 4.0D | +2,5 | 0.8 | ||
| 16 | 1,2-1,4 | 6600 | 0.6 | 1,4E | +6 | 1 | ||
| 18 | 0,65-0,75 | 2400 | 0.6 | 4.0D | +2,5 | 0.8 | ||
| 18 | 0.8 | 6600 | 0.6 | 1,6 S | +12 | 0.3 | ||
| 20 | 0,5-0,6 | 2400 | 0.6 | 4.0D | +3 | 0.8 | ||
| 20 | 0,6-0,9 | 6600 | 0.6 | 1,6 S | +13 | 0.3 | ||
| 22 | 0,45-0,5 | 2400 | 0.6 | 4.0D | +3 | 0.8 | ||
| 22 | 0,5-0,6 | 6600 | 0.6 | 1,6 S | +13 | 0.3 | ||
| 25 | 0.5 | 2400 | 0.5 | 5.0D | +3 | 1 | ||
| 25 | 0,4-0,5 | 6600 | 0.6 | 1,8 S | +14 | 0.3 | ||
| Stal nierdzewna | 1 | 40-50 | 6600 | N₂ | 10 | 1,5 S | 0 | 0.8 |
| 2 | 30-35 | 12 | 2,0 S | -1 | 0.5 | |||
| 3 | 18-26 | 12 | 2,5 S | -1.5 | 0.5 | |||
| 4 | 12-16 | 14 | 2,5 S | -2 | 0.5 | |||
| 5 | 8-9 | 14 | 3,0 S | -2.5 | 0.5 | |||
| 6 | 7-8 | 15 | 3,0 S | -3 | 0.5 | |||
| 8 | 3,5-4,5 | 15 | 3,0 S | -4 | 0.5 | |||
| 10 | 1,8-2,4 | 15 | 3,5 S | -6 | 0.5 | |||
| 12 | 1,2-1,5 | 16 | 3,5 S | -7.5 | 0.5 | |||
| 14 | 1-1.2 | 16 | 4,0 S | -9 | 0.5 | |||
| 16 | 0,5-0,7 | 18 | 4,0 S | -10.5 | 0.5 | |||
| 18 | 0,4-0,6 | 20 | 5,0 S | -11 | 0.3 | |||
| 20 | 0,3-0,4 | 20 | 5,0 S | -12 | 0.3 | |||
| Stop aluminium | 1 | 40-50 | 6600 | N₂ | 12 | 1,5 S | 0 | 1 |
| 2 | 25-30 | 12 | 2,0 S | -1 | 0.5 | |||
| 3 | 16-18 | 14 | 2,5 S | -1.5 | 0.5 | |||
| 4 | 10-14 | 14 | 2,5 S | -2 | 0.5 | |||
| 5 | 5-7 | 14 | 3,0 S | -3 | 0.5 | |||
| 6 | 3,5-4,5 | 16 | 3,0 S | -3 | 0.5 | |||
| 8 | 1,5-2,2 | 16 | 3,0 S | -4 | 0.5 | |||
| 10 | 1-1,5 | 18 | 3,5 S | -4.5 | 0.5 | |||
| 12 | 0,6-0,8 | 18 | 4,0 S | -5 | 0.5 | |||
| 14 | 0,4-0,6 | 18 | 4,0 S | -5 | 0.3 | |||
| 16 | 0,3-0,4 | 20 | 5,0 S | -8 | 0.3 | |||
| Mosiądz | 1 | 40-50 | 6600 | N₂ | 12 | 1,5 S | 0 | 1 |
| 2 | 25-30 | 12 | 2,0 S | -1 | 0.5 | |||
| 3 | 14-18 | 14 | 2,5 S | -1 | 0.5 | |||
| 4 | 10-12 | 14 | 3,0 S | -1.5 | 0.5 | |||
| 5 | 5-6 | 14 | 3,0 S | -2 | 0.5 | |||
| 6 | 3,5-4,5 | 16 | 3,0 S | -2.5 | 0.5 | |||
| 8 | 1,5-2 | 16 | 3,5 S | -3 | 0.5 | |||
| 10 | 0,8-1,2 | 16 | 3,5 S | -3 | 0.5 | |||
| 12 | 0,5-0,8 | 18 | 4,0 S | -4 | 0.3 | |||
| Miedź | 1 | 25-30 | 6600 | O₂ | 5 | 2,0 S | -0.5 | 1 |
| 2 | 13-16 | 5 | 2,0 S | -1 | 0.5 | |||
| 3 | 8-10 | 5 | 2,0 S | -2 | 0.5 | |||
| 4 | 5-6 | 6 | 2,0 S | -2 | 0.5 | |||
| 5 | 3-4 | 6 | 2,5 S | -3 | 0.5 | |||
| 6 | 1,5-2,5 | 8 | 2,5 S | -3 | 0.5 | |||
Uwaga: Parametry zaznaczone w tabeli na czerwono są parametrami prototypowymi. Na parametry te duży wpływ mają różne czynniki podczas rzeczywistego przetwarzania, dlatego nadają się one tylko do produkcji małych partii i nie są zalecane do produkcji i przetwarzania dużych partii. Wskazane jest użycie lasera o większej mocy.