Dilihat: 0 Penulis: Editor Situs Waktu Publikasi: 22-10-2025 Asal: Lokasi
| model laser | RFL-3000(34u) | Rasio Optik Kepala Pemotongan | 150Kolimasi 100 / Panjang Fokus 150 | |||||
| Bahan | Ketebalan [mm] | Kecepatan [m/mnt] | Kekuatan [W] | Gas | Tekanan Udara [bar] | Nosel [mm] | Posisi Fokus [mm] | Tinggi Pemotongan [mm] |
| Baja Karbon | 1 | 40-50 | 6600 | N₂/Udara | 12 | 1,5S | 0 | 1 |
| 2 | 25-30 | 12 | 2.0S | -1 | 0.5 | |||
| 3 | 18-24 | 14 | 2.0S | -1.5 | 0.5 | |||
| 4 | 12-16 | 14 | 2.0S | -2 | 0.5 | |||
| 5 | 8-10 | 16 | 3.0S | -2.5 | 0.5 | |||
| 6 | 7-8 | 16 | 3,5S | -3 | 0.5 | |||
| Baja Karbon | 3 | 3.6-4.2 | 2400 | O₂ | 0.6 | 1.2E | +3 | 0.8 |
| 4 | 3.3-3.8 | 2400 | 0.6 | 1.2E | +3 | 0.8 | ||
| 5 | 3-3.6 | 3500 | 0.6 | 1.2E | +3 | 0.8 | ||
| 6 | 2.7-3.2 | 3300 | 0.6 | 1.2E | +3 | 0.8 | ||
| 8 | 2.2-2.5 | 4200 | 0.6 | 1.2E | +3 | 0.8 | ||
| 10 | 2.0-2.3 | 6600 | 0.6 | 1.2E | +4 | 0.8 | ||
| 12 | 0,9-1 | 2400 | 0.6 | 3.0D | +2.5 | 0.8 | ||
| 12 | 1.9-2.1 | 6600 | 0.6 | 1.2E | +5 | 0.8 | ||
| 14 | 0,8-0,9 | 2400 | 0.6 | 3.5D | +2.5 | 0.8 | ||
| 14 | 1.4-1.7 | 6600 | 0.6 | 1.4E | +5 | 1 | ||
| 16 | 0,8-0,9 | 2400 | 0.6 | 4.0D | +2.5 | 0.8 | ||
| 16 | 1.2-1.4 | 6600 | 0.6 | 1.4E | +6 | 1 | ||
| 18 | 0,65-0,75 | 2400 | 0.6 | 4.0D | +2.5 | 0.8 | ||
| 18 | 0.8 | 6600 | 0.6 | 1.6S | +12 | 0.3 | ||
| 20 | 0,5-0,6 | 2400 | 0.6 | 4.0D | +3 | 0.8 | ||
| 20 | 0,6-0,9 | 6600 | 0.6 | 1.6S | +13 | 0.3 | ||
| 22 | 0,45-0,5 | 2400 | 0.6 | 4.0D | +3 | 0.8 | ||
| 22 | 0,5-0,6 | 6600 | 0.6 | 1.6S | +13 | 0.3 | ||
| 25 | 0.5 | 2400 | 0.5 | 5.0D | +3 | 1 | ||
| 25 | 0,4-0,5 | 6600 | 0.6 | 1.8S | +14 | 0.3 | ||
| Baja Tahan Karat | 1 | 40-50 | 6600 | N₂ | 10 | 1,5S | 0 | 0.8 |
| 2 | 30-35 | 12 | 2.0S | -1 | 0.5 | |||
| 3 | 18-26 | 12 | 2.5S | -1.5 | 0.5 | |||
| 4 | 12-16 | 14 | 2.5S | -2 | 0.5 | |||
| 5 | 8-9 | 14 | 3.0S | -2.5 | 0.5 | |||
| 6 | 7-8 | 15 | 3.0S | -3 | 0.5 | |||
| 8 | 3.5-4.5 | 15 | 3.0S | -4 | 0.5 | |||
| 10 | 1.8-2.4 | 15 | 3,5S | -6 | 0.5 | |||
| 12 | 1.2-1.5 | 16 | 3,5S | -7.5 | 0.5 | |||
| 14 | 1-1.2 | 16 | 4.0S | -9 | 0.5 | |||
| 16 | 0,5-0,7 | 18 | 4.0S | -10.5 | 0.5 | |||
| 18 | 0,4-0,6 | 20 | 5.0S | -11 | 0.3 | |||
| 20 | 0,3-0,4 | 20 | 5.0S | -12 | 0.3 | |||
| Paduan Aluminium | 1 | 40-50 | 6600 | N₂ | 12 | 1,5S | 0 | 1 |
| 2 | 25-30 | 12 | 2.0S | -1 | 0.5 | |||
| 3 | 16-18 | 14 | 2.5S | -1.5 | 0.5 | |||
| 4 | 10-14 | 14 | 2.5S | -2 | 0.5 | |||
| 5 | 5-7 | 14 | 3.0S | -3 | 0.5 | |||
| 6 | 3.5-4.5 | 16 | 3.0S | -3 | 0.5 | |||
| 8 | 1.5-2.2 | 16 | 3.0S | -4 | 0.5 | |||
| 10 | 1-1.5 | 18 | 3,5S | -4.5 | 0.5 | |||
| 12 | 0,6-0,8 | 18 | 4.0S | -5 | 0.5 | |||
| 14 | 0,4-0,6 | 18 | 4.0S | -5 | 0.3 | |||
| 16 | 0,3-0,4 | 20 | 5.0S | -8 | 0.3 | |||
| Kuningan | 1 | 40-50 | 6600 | N₂ | 12 | 1,5S | 0 | 1 |
| 2 | 25-30 | 12 | 2.0S | -1 | 0.5 | |||
| 3 | 14-18 | 14 | 2.5S | -1 | 0.5 | |||
| 4 | 10-12 | 14 | 3.0S | -1.5 | 0.5 | |||
| 5 | 5-6 | 14 | 3.0S | -2 | 0.5 | |||
| 6 | 3.5-4.5 | 16 | 3.0S | -2.5 | 0.5 | |||
| 8 | 1,5-2 | 16 | 3,5S | -3 | 0.5 | |||
| 10 | 0.8-1.2 | 16 | 3,5S | -3 | 0.5 | |||
| 12 | 0,5-0,8 | 18 | 4.0S | -4 | 0.3 | |||
| Tembaga | 1 | 25-30 | 6600 | O₂ | 5 | 2.0S | -0.5 | 1 |
| 2 | 13-16 | 5 | 2.0S | -1 | 0.5 | |||
| 3 | 8-10 | 5 | 2.0S | -2 | 0.5 | |||
| 4 | 5-6 | 6 | 2.0S | -2 | 0.5 | |||
| 5 | 3-4 | 6 | 2.5S | -3 | 0.5 | |||
| 6 | 1.5-2.5 | 8 | 2.5S | -3 | 0.5 | |||
Catatan: Parameter yang ditandai dengan warna merah pada tabel adalah parameter prototipe. Parameter ini sangat dipengaruhi oleh berbagai faktor selama pemrosesan sebenarnya, sehingga hanya cocok untuk produksi dalam jumlah kecil dan tidak direkomendasikan untuk produksi dan pemrosesan dalam jumlah besar. Disarankan untuk menggunakan laser dengan kekuatan lebih tinggi.