Aufrufe: 0 Autor: Site-Editor Veröffentlichungszeit: 22.10.2025 Herkunft: Website
| Lasermodell | RFL-3000(34u) | Optisches Verhältnis des Schneidkopfes | 150Kollimation 100 / Brennweite 150 | |||||||
| Material | Dicke [mm] | Geschwindigkeit [m/min] | Leistung [W] | Gas | Luftdruck [bar] | Düse [mm] | Fokusposition [mm] | Schnitthöhe [mm] | ||
| Kohlenstoffstahl | 1 | 45-60 | 6000 | N₂/Luft | 6 | 1,5S | 0 | 1 | ||
| 2 | 35-40 | 6 | 2,0S | -1 | 0.5 | |||||
| 3 | 22-27 | 6 | 2,0S | -1.5 | 0.5 | |||||
| 4 | 15-20 | 8 | 2,0S | -2 | 0.5 | |||||
| 5 | 9-12 | 8 | 3,0S | -2.5 | 0.5 | |||||
| 6 | 8-10 | 8 | 3,5S | -3 | 0.5 | |||||
| Kohlenstoffstahl | 3 | 3.6-4.2 | 2400 | O₂ | 0.6 | 1.2E | +3 | 0.8 | ||
| 4 | 3.2-3.4 | 2400 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 5 | 3-3.2 | 3000 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 6 | 2,7-2,9 | 3000 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 8 | 2.2-2.4 | 4500 | 0.6 | 1.2E | +5 | 0.8 | ||||
| 10 | 2,0-2,2 | 6000 | 0.6 | 1.2E | +7 | 0.8 | ||||
| 12 | 0,9-1 | 2400 | 0.6 | 3.0D | +4,5 | 0.8 | ||||
| 12 | 1.9-2.1 | 6000 | 0.6 | 1.2E | +9 | 0.8 | ||||
| 14 | 0,8-0,9 | 2400 | 0.6 | 3.5D | +5 | 0.8 | ||||
| 14 | 1,4-1,6 | 6000 | 0.6 | 1.4E | +12 | 0.8 | ||||
| 16 | 0,7-0,8 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 16 | 1.2-1.4 | 6000 | 0.6 | 1.4E | +13 | 0.8 | ||||
| 18 | 0,55-0,65 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 18 | 0.8 | 6000 | 0.6 | 1.4E | +13 | 0.3 | ||||
| 20 | 0,5-0,6 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 20 | 0,6-0,8 | 6000 | 0.75 | 1.4E | +13,5 | 0.3 | ||||
| 22 | 0,45-0,5 | 2400 | 0.6 | 4.5D | +5,5 | 0.8 | ||||
| 22 | 0,5-0,6 | 6000 | 0.75 | 1,5S | +13,5 | 0.3 | ||||
| 25 | 0.55 | 2700 | 0.6 | 5.0D | +5,5 | 0.8 | ||||
| 25 | 0,4-0,5 | 6000 | 0.75 | 1,5S | +14 | 0.3 | ||||
| 30 | 0.3 | 6000 | 1 | 1,5S | +14 | 0.3 | ||||
| Edelstahl | 1 | 45-60 | 6000 | N₂ | 10 | 1,5S | 0 | 0.8 | ||
| 2 | 35-45 | 12 | 2,0S | -1 | 0.5 | |||||
| 3 | 22-27 | 12 | 2,5S | -1.5 | 0.5 | |||||
| 4 | 15-20 | 14 | 2,5S | -2 | 0.5 | |||||
| 5 | 9-12 | 14 | 3,0S | -2.5 | 0.5 | |||||
| 6 | 8-11 | 15 | 3,0S | -3 | 0.5 | |||||
| 8 | 3,5-4,5 | 15 | 3,0S | -4 | 0.5 | |||||
| 10 | 2-2,5 | 15 | 3,5B | -6 | 0.5 | |||||
| 12 | 1,5-1,8 | 16 | 3,5B | -7.5 | 0.5 | |||||
| 14 | 1-1,5 | 16 | 4,0B | -9 | 0.5 | |||||
| 16 | 0,5-0,6 | 18 | 4,0B | -14 | 0.5 | |||||
| 18 | 0,3-0,5 | 20 | 5,0B | -15 | 0.3 | 300 | 60 | |||
| 20 | 0,2-0,25 | 20 | 5,0B | -16 | 0.3 | 300 | 60 | |||
| Aluminiumlegierung | 1 | 45-60 | 6000 | N₂ | 12 | 1,5S | 0 | 1 | ||
| 2 | 35-40 | 12 | 2,0S | -1 | 0.5 | |||||
| 3 | 22-27 | 14 | 2,5S | -1.5 | 0.5 | |||||
| 4 | 14-17 | 14 | 2,5S | -2 | 0.5 | |||||
| 5 | 9-11 | 14 | 3,0S | -3 | 0.5 | |||||
| 6 | 4-6 | 16 | 3,0S | -3 | 0.5 | |||||
| 8 | 2,5-3 | 16 | 3,0S | -7 | 0.5 | |||||
| 10 | 1,5-1,8 | 18 | 3,5B | -8 | 0.5 | |||||
| 12 | 0,8-1 | 18 | 4,0B | -8 | 0.5 | |||||
| 14 | 0,6-0,7 | 18 | 4,0B | -9 | 0.3 | |||||
| 16 | 0,35-0,45 | 20 | 5,0B | -12 | 0.3 | |||||
| 20 | 0,2-0,3 | 20 | 5,0B | -13 | 0.3 | |||||
| Messing | 1 | 45-55 | 6000 | N₂ | 12 | 1,5S | 0 | 1 | ||
| 2 | 30-35 | 12 | 2,0S | -1 | 0.5 | |||||
| 3 | 18-25 | 14 | 2,5S | -2 | 0.5 | |||||
| 4 | 12-15 | 14 | 3,0S | -3 | 0.5 | |||||
| 5 | 4,5-6 | 14 | 3,0S | -4 | 0.5 | |||||
| 6 | 3,5-4 | 16 | 3,0S | -5 | 0.5 | |||||
| 8 | 2-2.6 | 16 | 3,5B | -6 | 0.5 | |||||
| 10 | 1-1.3 | 16 | 3,5B | -8 | 0.5 | |||||
| 12 | 0,6-0,8 | 18 | 4,0S | -8 | 0.3 | |||||
| Kupfer | 1 | 25-30 | 6000 | O₂ | 5 | 2,0S | -0.5 | 1 | ||
| 2 | 13-16 | 5 | 2,0S | -1 | 0.5 | |||||
| 3 | 8-10 | 5 | 2,0S | -2 | 0.5 | |||||
| 4 | 5-6 | 6 | 2,0S | -2 | 0.5 | |||||
| 5 | 3-4 | 6 | 2,5S | -3 | 0.5 | |||||
| 6 | 1,5-2,5 | 8 | 2,5S | -3 | 0.5 | |||||
Hinweis: Die in der Tabelle rot markierten Parameter sind Prototypparameter. Diese Parameter werden während der tatsächlichen Verarbeitung stark von verschiedenen Faktoren beeinflusst, sodass sie nur für die Produktion kleiner Chargen geeignet sind und nicht für die Produktion und Verarbeitung großer Chargen empfohlen werden. Es empfiehlt sich, einen Laser mit höherer Leistung zu verwenden.