Bekeken: 0 Auteur: Site-editor Publicatietijd: 22-10-2025 Herkomst: Locatie
| Lasermodel | RFL-3000(34u) | Optische verhouding snijkop | 150Collimatie 100 / Brandpuntsafstand 150 | |||||||
| Materiaal | Dikte [mm] | Snelheid [m/min] | Vermogen [W] | Gas | Luchtdruk [bar] | Mondstuk [mm] | Brandpuntspositie [mm] | Maaihoogte [mm] | ||
| Koolstofstaal | 1 | 45-60 | 6000 | N₂/Lucht | 6 | 1,5S | 0 | 1 | ||
| 2 | 35-40 | 6 | 2,0S | -1 | 0.5 | |||||
| 3 | 22-27 | 6 | 2,0S | -1.5 | 0.5 | |||||
| 4 | 15-20 | 8 | 2,0S | -2 | 0.5 | |||||
| 5 | 9-12 | 8 | 3,0S | -2.5 | 0.5 | |||||
| 6 | 8-10 | 8 | 3,5S | -3 | 0.5 | |||||
| Koolstofstaal | 3 | 3.6-4.2 | 2400 | O₂ | 0.6 | 1.2E | +3 | 0.8 | ||
| 4 | 3.2-3.4 | 2400 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 5 | 3-3.2 | 3000 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 6 | 2,7-2,9 | 3000 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 8 | 2.2-2.4 | 4500 | 0.6 | 1.2E | +5 | 0.8 | ||||
| 10 | 2,0-2,2 | 6000 | 0.6 | 1.2E | +7 | 0.8 | ||||
| 12 | 0,9-1 | 2400 | 0.6 | 3.0D | +4,5 | 0.8 | ||||
| 12 | 1.9-2.1 | 6000 | 0.6 | 1.2E | +9 | 0.8 | ||||
| 14 | 0,8-0,9 | 2400 | 0.6 | 3.5D | +5 | 0.8 | ||||
| 14 | 1,4-1,6 | 6000 | 0.6 | 1,4E | +12 | 0.8 | ||||
| 16 | 0,7-0,8 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 16 | 1,2-1,4 | 6000 | 0.6 | 1,4E | +13 | 0.8 | ||||
| 18 | 0,55-0,65 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 18 | 0.8 | 6000 | 0.6 | 1,4E | +13 | 0.3 | ||||
| 20 | 0,5-0,6 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 20 | 0,6-0,8 | 6000 | 0.75 | 1,4E | +13,5 | 0.3 | ||||
| 22 | 0,45-0,5 | 2400 | 0.6 | 4.5D | +5,5 | 0.8 | ||||
| 22 | 0,5-0,6 | 6000 | 0.75 | 1,5S | +13,5 | 0.3 | ||||
| 25 | 0.55 | 2700 | 0.6 | 5.0D | +5,5 | 0.8 | ||||
| 25 | 0,4-0,5 | 6000 | 0.75 | 1,5S | +14 | 0.3 | ||||
| 30 | 0.3 | 6000 | 1 | 1,5S | +14 | 0.3 | ||||
| Roestvrij staal | 1 | 45-60 | 6000 | N₂ | 10 | 1,5S | 0 | 0.8 | ||
| 2 | 35-45 | 12 | 2,0S | -1 | 0.5 | |||||
| 3 | 22-27 | 12 | 2,5S | -1.5 | 0.5 | |||||
| 4 | 15-20 | 14 | 2,5S | -2 | 0.5 | |||||
| 5 | 9-12 | 14 | 3,0S | -2.5 | 0.5 | |||||
| 6 | 8-11 | 15 | 3,0S | -3 | 0.5 | |||||
| 8 | 3,5-4,5 | 15 | 3,0S | -4 | 0.5 | |||||
| 10 | 2-2,5 | 15 | 3,5 miljard | -6 | 0.5 | |||||
| 12 | 1,5-1,8 | 16 | 3,5 miljard | -7.5 | 0.5 | |||||
| 14 | 1-1,5 | 16 | 4,0B | -9 | 0.5 | |||||
| 16 | 0,5-0,6 | 18 | 4,0B | -14 | 0.5 | |||||
| 18 | 0,3-0,5 | 20 | 5,0B | -15 | 0.3 | 300 | 60 | |||
| 20 | 0,2-0,25 | 20 | 5,0B | -16 | 0.3 | 300 | 60 | |||
| Aluminiumlegering | 1 | 45-60 | 6000 | N₂ | 12 | 1,5S | 0 | 1 | ||
| 2 | 35-40 | 12 | 2,0S | -1 | 0.5 | |||||
| 3 | 22-27 | 14 | 2,5S | -1.5 | 0.5 | |||||
| 4 | 14-17 | 14 | 2,5S | -2 | 0.5 | |||||
| 5 | 9-11 | 14 | 3,0S | -3 | 0.5 | |||||
| 6 | 4-6 | 16 | 3,0S | -3 | 0.5 | |||||
| 8 | 2,5-3 | 16 | 3,0S | -7 | 0.5 | |||||
| 10 | 1,5-1,8 | 18 | 3,5 miljard | -8 | 0.5 | |||||
| 12 | 0,8-1 | 18 | 4,0B | -8 | 0.5 | |||||
| 14 | 0,6-0,7 | 18 | 4,0B | -9 | 0.3 | |||||
| 16 | 0,35-0,45 | 20 | 5,0B | -12 | 0.3 | |||||
| 20 | 0,2-0,3 | 20 | 5,0B | -13 | 0.3 | |||||
| Messing | 1 | 45-55 | 6000 | N₂ | 12 | 1,5S | 0 | 1 | ||
| 2 | 30-35 | 12 | 2,0S | -1 | 0.5 | |||||
| 3 | 18-25 | 14 | 2,5S | -2 | 0.5 | |||||
| 4 | 12-15 | 14 | 3,0S | -3 | 0.5 | |||||
| 5 | 4,5-6 | 14 | 3,0S | -4 | 0.5 | |||||
| 6 | 3,5-4 | 16 | 3,0S | -5 | 0.5 | |||||
| 8 | 2-2,6 | 16 | 3,5 miljard | -6 | 0.5 | |||||
| 10 | 1-1.3 | 16 | 3,5 miljard | -8 | 0.5 | |||||
| 12 | 0,6-0,8 | 18 | 4,0S | -8 | 0.3 | |||||
| Koper | 1 | 25-30 | 6000 | O₂ | 5 | 2,0S | -0.5 | 1 | ||
| 2 | 13-16 | 5 | 2,0S | -1 | 0.5 | |||||
| 3 | 8-10 | 5 | 2,0S | -2 | 0.5 | |||||
| 4 | 5-6 | 6 | 2,0S | -2 | 0.5 | |||||
| 5 | 3-4 | 6 | 2,5S | -3 | 0.5 | |||||
| 6 | 1,5-2,5 | 8 | 2,5S | -3 | 0.5 | |||||
Opmerking: De rood gemarkeerde parameters in de tabel zijn prototypeparameters. Deze parameters worden tijdens de daadwerkelijke verwerking sterk beïnvloed door verschillende factoren. Daarom zijn ze alleen geschikt voor de productie van kleine batches en worden ze niet aanbevolen voor de productie en verwerking van grote batches. Het is raadzaam een laser met een hoger vermogen te gebruiken.