Zobrazení: 0 Autor: Editor webu Čas publikování: 22. 10. 2025 Původ: místo
| Laserový model | RFL-3000 (34u) | Optický poměr řezací hlavy | 150Kolimace 100 / Ohnisková vzdálenost 150 | |||||||
| Materiál | Tloušťka [mm] | Rychlost [m/min] | Výkon [W] | Plyn | Tlak vzduchu [bar] | Tryska [mm] | Ohnisková poloha [mm] | Výška řezu [mm] | ||
| Uhlíková ocel | 1 | 45-60 | 6000 | N₂/vzduch | 6 | 1,5 S | 0 | 1 | ||
| 2 | 35-40 | 6 | 2,0 s | -1 | 0.5 | |||||
| 3 | 22-27 | 6 | 2,0 s | -1.5 | 0.5 | |||||
| 4 | 15-20 | 8 | 2,0 s | -2 | 0.5 | |||||
| 5 | 9-12 | 8 | 3,0 s | -2.5 | 0.5 | |||||
| 6 | 8-10 | 8 | 3,5 S | -3 | 0.5 | |||||
| Uhlíková ocel | 3 | 3,6-4,2 | 2400 | O₂ | 0.6 | 1,2E | +3 | 0.8 | ||
| 4 | 3,2-3,4 | 2400 | 0.6 | 1,2E | +3 | 0.8 | ||||
| 5 | 3-3.2 | 3000 | 0.6 | 1,2E | +3 | 0.8 | ||||
| 6 | 2,7-2,9 | 3000 | 0.6 | 1,2E | +3 | 0.8 | ||||
| 8 | 2,2-2,4 | 4500 | 0.6 | 1,2E | +5 | 0.8 | ||||
| 10 | 2,0-2,2 | 6000 | 0.6 | 1,2E | +7 | 0.8 | ||||
| 12 | 0,9-1 | 2400 | 0.6 | 3.0D | +4,5 | 0.8 | ||||
| 12 | 1,9-2,1 | 6000 | 0.6 | 1,2E | +9 | 0.8 | ||||
| 14 | 0,8-0,9 | 2400 | 0.6 | 3.5D | +5 | 0.8 | ||||
| 14 | 1,4-1,6 | 6000 | 0.6 | 1.4E | +12 | 0.8 | ||||
| 16 | 0,7-0,8 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 16 | 1,2-1,4 | 6000 | 0.6 | 1.4E | +13 | 0.8 | ||||
| 18 | 0,55-0,65 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 18 | 0.8 | 6000 | 0.6 | 1.4E | +13 | 0.3 | ||||
| 20 | 0,5-0,6 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 20 | 0,6-0,8 | 6000 | 0.75 | 1.4E | +13,5 | 0.3 | ||||
| 22 | 0,45-0,5 | 2400 | 0.6 | 4.5D | +5,5 | 0.8 | ||||
| 22 | 0,5-0,6 | 6000 | 0.75 | 1,5 S | +13,5 | 0.3 | ||||
| 25 | 0.55 | 2700 | 0.6 | 5.0D | +5,5 | 0.8 | ||||
| 25 | 0,4-0,5 | 6000 | 0.75 | 1,5 S | +14 | 0.3 | ||||
| 30 | 0.3 | 6000 | 1 | 1,5 S | +14 | 0.3 | ||||
| Nerez | 1 | 45-60 | 6000 | N₂ | 10 | 1,5 S | 0 | 0.8 | ||
| 2 | 35-45 | 12 | 2,0 s | -1 | 0.5 | |||||
| 3 | 22-27 | 12 | 2,5 S | -1.5 | 0.5 | |||||
| 4 | 15-20 | 14 | 2,5 S | -2 | 0.5 | |||||
| 5 | 9-12 | 14 | 3,0 s | -2.5 | 0.5 | |||||
| 6 | 8-11 | 15 | 3,0 s | -3 | 0.5 | |||||
| 8 | 3,5-4,5 | 15 | 3,0 s | -4 | 0.5 | |||||
| 10 | 2-2,5 | 15 | 3,5B | -6 | 0.5 | |||||
| 12 | 1,5-1,8 | 16 | 3,5B | -7.5 | 0.5 | |||||
| 14 | 1-1,5 | 16 | 4,0B | -9 | 0.5 | |||||
| 16 | 0,5-0,6 | 18 | 4,0B | -14 | 0.5 | |||||
| 18 | 0,3-0,5 | 20 | 5,0B | -15 | 0.3 | 300 | 60 | |||
| 20 | 0,2-0,25 | 20 | 5,0B | -16 | 0.3 | 300 | 60 | |||
| Hliníková slitina | 1 | 45-60 | 6000 | N₂ | 12 | 1,5 S | 0 | 1 | ||
| 2 | 35-40 | 12 | 2,0 s | -1 | 0.5 | |||||
| 3 | 22-27 | 14 | 2,5 S | -1.5 | 0.5 | |||||
| 4 | 14-17 | 14 | 2,5 S | -2 | 0.5 | |||||
| 5 | 9-11 | 14 | 3,0 s | -3 | 0.5 | |||||
| 6 | 4-6 | 16 | 3,0 s | -3 | 0.5 | |||||
| 8 | 2,5-3 | 16 | 3,0 s | -7 | 0.5 | |||||
| 10 | 1,5-1,8 | 18 | 3,5B | -8 | 0.5 | |||||
| 12 | 0,8-1 | 18 | 4,0B | -8 | 0.5 | |||||
| 14 | 0,6-0,7 | 18 | 4,0B | -9 | 0.3 | |||||
| 16 | 0,35-0,45 | 20 | 5,0B | -12 | 0.3 | |||||
| 20 | 0,2-0,3 | 20 | 5,0B | -13 | 0.3 | |||||
| Mosaz | 1 | 45-55 | 6000 | N₂ | 12 | 1,5 S | 0 | 1 | ||
| 2 | 30-35 | 12 | 2,0 s | -1 | 0.5 | |||||
| 3 | 18-25 | 14 | 2,5 S | -2 | 0.5 | |||||
| 4 | 12-15 | 14 | 3,0 s | -3 | 0.5 | |||||
| 5 | 4,5-6 | 14 | 3,0 s | -4 | 0.5 | |||||
| 6 | 3,5-4 | 16 | 3,0 s | -5 | 0.5 | |||||
| 8 | 2-2.6 | 16 | 3,5B | -6 | 0.5 | |||||
| 10 | 1-1,3 | 16 | 3,5B | -8 | 0.5 | |||||
| 12 | 0,6-0,8 | 18 | 4,0 s | -8 | 0.3 | |||||
| Měď | 1 | 25-30 | 6000 | O₂ | 5 | 2,0 s | -0.5 | 1 | ||
| 2 | 13-16 | 5 | 2,0 s | -1 | 0.5 | |||||
| 3 | 8-10 | 5 | 2,0 s | -2 | 0.5 | |||||
| 4 | 5-6 | 6 | 2,0 s | -2 | 0.5 | |||||
| 5 | 3-4 | 6 | 2,5 S | -3 | 0.5 | |||||
| 6 | 1,5-2,5 | 8 | 2,5 S | -3 | 0.5 | |||||
Poznámka: Parametry označené v tabulce červeně jsou parametry prototypu. Tyto parametry jsou při vlastním zpracování značně ovlivněny různými faktory, proto jsou vhodné pouze pro malosériovou výrobu a nedoporučují se pro velkosériovou výrobu a zpracování. Je vhodné použít laser s vyšším výkonem.