Wyświetlenia: 0 Autor: Edytor witryny Czas publikacji: 22.10.2025 Pochodzenie: Strona
| Model lasera | RFL-3000(34u) | Współczynnik optyczny głowicy tnącej | 150Kolimacja 100 / Ogniskowa 150 | |||||||
| 材料 | Średnica [mm] | 速度[m/min] | 功率 [W] | 气体 | 气压 [bar] | Średnica [mm] | Średnica [mm] | 切割高度[mm] | 频率[HZ] | 占空比[%] |
| Tworzywo | Grubość [mm] | Prędkość [m/min] | Moc [W] | Gaz | Ciśnienie powietrza [bar] | Dysza [mm] | Pozycja ogniskowa [mm] | Wysokość cięcia [mm] | ||
| Stal węglowa | 1 | 40-50 | 5000 | N₂/powietrze | 6 | 1,5 S | 0 | 1 | ||
| 2 | 30-35 | 6 | 2,0 S | -1 | 0.5 | |||||
| 3 | 20-25 | 6 | 2,0 S | -1.5 | 0.5 | |||||
| 4 | 13-18 | 8 | 2,0 S | -2 | 0.5 | |||||
| 5 | 8-10 | 8 | 3,0 S | -2.5 | 0.5 | |||||
| 6 | 6-8 | 8 | 3,5 S | -3 | 0.5 | |||||
| Stal węglowa | 3 | 3.6-4.2 | 2400 | O₂ | 0.6 | 1.2E | +3 | 0.8 | ||
| 4 | 3.2-3.4 | 2400 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 5 | 3-3.2 | 3000 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 6 | 2,7-2,9 | 3000 | 0.6 | 1.2E | +3 | 0.8 | ||||
| 8 | 2.2-2.4 | 4500 | 0.6 | 1.2E | +5 | 0.8 | ||||
| 12 | 0,9-1 | 2400 | 0.6 | 3.0D | +4,5 | 0.8 | ||||
| 14 | 0,8-0,9 | 2400 | 0.6 | 3.5D | +5 | 0.8 | ||||
| 16 | 0,7-0,8 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 18 | 0,55-0,65 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 20 | 0,5-0,6 | 2400 | 0.6 | 4.0D | +5,5 | 0.8 | ||||
| 22 | 0,45-0,5 | 2400 | 0.6 | 4.5D | +5,5 | 0.8 | ||||
| Stal nierdzewna | 1 | 40-50 | 5000 | N₂ | 10 | 1,5 S | 0 | 0.8 | ||
| 2 | 30-35 | 12 | 2,0 S | -1 | 0.5 | |||||
| 3 | 20-25 | 12 | 2,5 S | -1.5 | 0.5 | |||||
| 4 | 13-18 | 14 | 2,5 S | -2 | 0.5 | |||||
| 5 | 8-10 | 14 | 3,0 S | -2.5 | 0.5 | |||||
| 6 | 6-8 | 15 | 3,0 S | -3 | 0.5 | |||||
| 8 | 3-4 | 15 | 3,0 S | -4 | 0.5 | |||||
| 10 | 1,8-2,2 | 15 | 3,5B | -6 | 0.5 | |||||
| 12 | 1,2-1,5 | 16 | 3,5B | -7.5 | 0.5 | |||||
| 14 | 0,8-1,2 | 16 | 4.0B | -9 | 0.5 | |||||
| 16 | 0,4-0,5 | 18 | 4.0B | -14 | 0.5 | |||||
| 18 | 0,3-0,4 | 20 | 5,0B | -15 | 0.3 | 300 | 60 | |||
| Stop aluminium | 1 | 35-45 | 5000 | N₂ | 12 | 1,5 S | 0 | 1 | ||
| 2 | 28-32 | 12 | 2,0 S | -1 | 0.5 | |||||
| 3 | 18-23 | 14 | 2,5 S | -1.5 | 0.5 | |||||
| 4 | 12-16 | 14 | 2,5 S | -2 | 0.5 | |||||
| 5 | 7-9 | 14 | 3,0 S | -3 | 0.5 | |||||
| 6 | 4-6 | 16 | 3,0 S | -3 | 0.5 | |||||
| 8 | 2,5-3 | 16 | 3,0 S | -7 | 0.5 | |||||
| 10 | 1,5-1,8 | 18 | 3,5B | -8 | 0.5 | |||||
| 12 | 0,8-1 | 18 | 4.0B | -8 | 0.5 | |||||
| 14 | 0,6-0,7 | 18 | 4.0B | -9 | 0.3 | |||||
| 16 | 0,35-0,45 | 20 | 5,0B | -12 | 0.3 | |||||
| Mosiądz | 1 | 30-40 | 5000 | N₂ | 12 | 1,5 S | 0 | 1 | ||
| 2 | 26-30 | 12 | 2,0 S | -1 | 0.5 | |||||
| 3 | 16-20 | 14 | 2,5 S | -2 | 0.5 | |||||
| 4 | 10-14 | 14 | 3,0 S | -3 | 0.5 | |||||
| 5 | 4,5-6 | 14 | 3,0 S | -4 | 0.5 | |||||
| 6 | 3,5-4 | 16 | 3,0 S | -5 | 0.5 | |||||
| 8 | 2-2.4 | 16 | 3,5B | -6 | 0.5 | |||||
| 10 | 1-1.3 | 16 | 3,5B | -8 | 0.5 | |||||
| Miedź | 1 | 20-25 | 5000 | O₂ | 5 | 2,0 S | -0.5 | 1 | ||
| 2 | 12-14 | 5 | 2,0 S | -1 | 0.5 | |||||
| 3 | 7-9 | 5 | 2,0 S | -2 | 0.5 | |||||
| 4 | 4-5 | 6 | 2,0 S | -2 | 0.5 | |||||
| 5 | 2,5-3,5 | 6 | 2,5 S | -3 | 0.5 | |||||
| 6 | 1,5-2 | 8 | 2,5 S | -3 | 0.5 | |||||
Uwaga: Parametry zaznaczone w tabeli na czerwono są parametrami prototypowymi. Na parametry te duży wpływ mają różne czynniki podczas rzeczywistego przetwarzania, dlatego nadają się one tylko do produkcji małych partii i nie są zalecane do produkcji i przetwarzania dużych partii. Wskazane jest użycie lasera o większej mocy.